Recent Studies of Corrosion - Fatigue Crack Growth on the 7081-T73511 Aluminium Alloy

Abstract

This work aims to evaluate the effect of localized corrosion on the fatigue crack growth (FCG) resistance of the 7081-T73511 aluminium alloy. The understanding of this complex combined process was explained by the dissolution of adjacent 7081-T73511 aluminium matrix promoted by the Al₇Cu₂Fe second-phase particle and the crack tip interaction time with the aggressive medium. Fracture surfaces produced in air and in sea water fog at the testing conditions applied here, basically present the same appearance, with a transgranular, cleavage-like cracking mode for 8 <DK< 30 values.